The Korean Society of Surface Science and Engineering

In this study, the effect of drying temperature on characteristics of the trivalent chromate film on electroplated zinc was investigated. An zinc-electroplated iron specimen with a thickness of 5 μm was used for chromate treatment. Chromate treatment was conducted in a solution diluted 10 times from a mixture of Cr(NO₃)₃∙9H₂0 360 g/L, Co(NO₃)₂∙6H₂O 60 g/L, Na₂SO₄ 60 g/L, NH₄F∙HF 25 g/L, and NaOH 20 g/L. The zinc electroplated specimen was treated using the chromate solution with pH 2.0 at 25 ℃ for 60 s. Subsequently, chromate-treated samples were dried in an electric furnace for 2h with temperature varied from 25 to 125 ℃. The corrosion rate increased with the increase in the drying temperature, and the surface morphology of the chromate-treated film was observed using FE-SEM. When the drying temperature changed, the color of the chromate film changed from green to yellow, and the thickness of the film changed from 362 to 241 nm, respectively. Additionally, corrosion resistance was evaluated via a salt spray test.

키워드 Zinc Electroplating; Chromate; Corrosion Resistance; Drying Tempareture; Film Color; Film Thickness