The Korean Society of Surface Science and Engineering

In this study, the nickel hydroxide (Ni(OH)₂) electrode for supercapacitor was prepared via hydrothermal method. Based on the nickel (Ni) foam, the electrode does not require any additional binder material or post-processing. Nickel nitrate (Ni(NO₃)₂) and hexamethylenetetramine (C₆H₁₂N₄) were used for synthesis, and the synthesis condition was 12 hours at 80 °C. X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM) were used to analyze the structural characteristics of the electrode, and it shown that the nickel hydroxide was successfully prepared after only the one-step hydrothermal synthesis. The electrochemical properties were analyzed through the half-cell test. The prepared electrode shown a pair of oxidation/reduction peaks, indicating that the driving method included the redox reaction on the electrode surface. After the charge/discharge test, the specific capacitance was calculated as the value of 438 F/g at 3 A/g.

키워드 Hydrothermal synthesis, Nickel hydroxide, Nickel foam, Supercapacitor